tempering temperature发音

意思翻译

[机]回火温度

相似词语短语

tempering───v.调和（temper的ing形式）；n.[机]回火

temperature───n.温度；体温；气温；发烧

tempering top───回火顶

critical temperature───[物][电子]临界温度；n.临界温度

temperature outside───室外温度

temperature rise───[电]温升；温度上升；温度上升，温升，升温

constant temperature───[热]恒温；定温；等温；等温，恒温

fluctuating temperature───波动温度；脉动温度；脉动温度，波动温度

low temperature───低温，低温度；[物]低温

双语使用场景

tempering temperature, the retained austenite decreases.───回火温度升高，其残余奥氏体量逐渐减少。

When tempering temperature further heightens, he hardness descends gradually.───当回火温度进一步升高时，硬度逐渐降低。

The hardenability is irrelevant to the isothermal tempering temperature.───淬透性与等温回火温度无关。

The tempered lath martensite grows up with the tempering temperature increasing, however the tendency of growing is not obvious.───随淬火加热温度的升高，板条马氏体逐渐长大，但长大趋势不明显；

With the elevating of the tempering temperature, the hardness can be increased and the wear resistance will be decreased.───随着回火温度的提高，深冷处理后的试样硬度升高，但耐磨性降低。

After tempering, the hardness and antibacterial property first increase then decrease with the increase of tempering temperature.───回火后，随回火温度的升高，硬度和抗菌率均呈先增大后减小的趋势；

the higher the tempering temperature, the lower the strength and hardness, and the better the plasticity and toughness are.───随着回火温度的升高，合金的强度、硬度越低，塑性、韧性越好。

With increasing tempering temperature, the retained austenite decreases.───回火温度升高，其残余奥氏体量逐渐减少。

The results show that quenching temperature, tempering temperature and holding time are determining factors.───结果表明：加热温度、回火温度、保温时间起着决定性作用；

英语使用场景

For acquiring good properties of brazed joint of coal cutter, the effect of tempering temperature on microstructure and shearing strength of brazed joint was studied.

Effects of tempering temperature on high carbon medium manganese steel has been investigated in present work.

Having studied the relationship between tempered hardness and tempering temperature for hardened carbon steels, a tempering behaviour model is set up between hardness and temperature.

The relationship between impact toughness and tempering temperature indicated secondary tempering brit - tleness peak at between 570 - 580.

Microalloy element V should be avoided adding , although it improves the strength at elevated tempering temperature , but reduces the ductility .